Product Description :
The JiuChen Ceramic wool blanket are made from long ceramic fibres, and through double needing without binders. They exists stability and good tensile strength in 1000C-1430C. They offer superior effects in saving heat energy and refractory field.
Item Name |
HZ 1430℃ ceramic fiber blanket factory china |
Size(mm) |
Length:7200/3600 Width: 1220/610 Thickness: 20-50 (Other sizes and shapes on request. ) |
Density(kg/m3) |
96,128 |
Package |
Carton with PVC film inner OR Woven Bag with PVC film inner |
Payment |
30% T/T in advance, balance at B/L copy |
Delivery time |
7-10 days after deposit |
MOQ |
As requested |
Supply Ability |
100t per month |
Samples |
Available, please contact Ivy |
Certificates |
ISO9001-2000 |
ITEM |
PRODUCT |
COM |
STD |
HP |
HA |
HZ |
|
Classification Temperature(ºC) |
1100(2012℉) |
1260(2300℉) |
1260(2300℉) |
1360(2480℉) |
1430(2606℉) |
||
Working Temperature(ºC) |
<1000(1832℉) |
1050(1922℉) |
1100(2012℉) |
1200(2192℉) |
1350(2462℉) |
||
Color |
Pure White |
Pure White |
Pure White |
Pure White |
Pure White |
||
Density(kg/m3) |
96-128kg/m3 |
96-128kg/m3 |
96-128kg/m3 |
128-160kg/m3 |
128-160kg/m3 |
||
Line Shrinkage (%) After 24hours |
≤2.5 (1000℃/1832℉) |
≤2.5 (1000℃/1832℉) |
≤2.5 (1100℃/2012℉) |
≤3.5 (1250℃/2282℉) |
≤3.5 (1350℃/2462℉) |
||
Thermal conductivity (w/m.k) density(128Kg/m3) |
0.09(400℃/752F) |
0.09(400℃/752F) |
0.09(400℃/752F) |
0.132(600℃/1112F) |
0.176(600/1112F) |
||
0.176 (800ºC/1472F) |
0.176 (800ºC/1472F) |
0.176 (800ºC/1472F) |
0.22 (1000ºC/1832F) |
0.22 (1000ºC/1832F) |
|||
|
|
0.22 (1000 ºC/1832F) |
0.28 (1200ºC/2192F) |
|
|||
Tensile strength (Mpa) |
0.04 |
0.04 |
0.04 |
0.04 |
0.04 |
||
Chemical Composition % |
Al2O3 |
44 |
46 |
47-49 |
52-55 |
39-40 |
|
Al2O3+SiO2 |
96 |
97 |
99 |
99 |
- |
||
Al2O3+SiO2+ZrO2 |
- |
- |
- |
- |
99 |
||
ZrO2 |
- |
- |
- |
- |
15-17 |
||
Fe2O3 |
<1.2 |
<1.0 |
0.2 |
0.2 |
0.2 |
||
Na2O+K2O |
≤0.5 |
≤0. 5 |
0.2 |
0.2 |
0.2 |
||
Size(mm) |
Specification:7200X610X25/3600x610x50,other according to customer's requirement |